Thermally stimulated depolarization current analysis for the dielectric aging of Mn and V-codoped BaTiO3 multi layer ceramic capacitor

Dielectric aging of Mn and V-codoped BaTiO3 was investigated. The increase of V concentration had little influence on aging, whereas that of Mn increased it. Thermally stimulated depolarization current (TSDC) of low Mn concentration specimen showed one peak, whereas Mn-increased specimen showed two peaks. The first and second peak is supposed to be caused by the phase transition of the undoped core region and the defect dipole of Mn such as MnTi″-VO•• or MnTi′-VO••, respectively. High TSDC associated with the defect dipole of Mn and significant aging rate experimentally demonstrates that the dielectric aging is controlled by the defect dipole.