Polymer-Rich Composite Electrolytes for All-Solid-State Li–S Cells

Polymer-rich composite electrolytes with lithium bis(fluorosulfonyl)imide/poly(ethylene oxide) (LiFSI/PEO) containing either Li-ion conducting glass ceramic (LICGC) or inorganic Al 2 O 3 fillers are investigated in all-solid-state Li–S cells. In the presence of the fillers, the ionic conductivity of the composite polymer electrolytes (CPEs) does not increase compared to the plain LiFSI/PEO electrolyte at various tested temperatures. The CPE with Al 2 O 3 fillers improves the stability of the Li/electrolyte interface, while the Li–S cell with a LICGC-based CPE delivers high sulfur utilization of 1111 mAh g –1 and areal capacity of 1.14 mAh cm –2 . In particular, the cell performance gets further enhanced when combining these two CPEs (Li | Al 2 O 3 –CPE/LICGC–CPE | S), reaching a capacity of 518 mAh g –1 and 0.53 mAh cm –2 with Coulombic efficiency higher than 99% at the end of 50 cycles at 70 °C. This study shows that the CPEs can be promising electrolyte candidates to develop safe and high-performance all-solid-state Li–S batteries.