Graftlike interpolymer complexes from poly(2‐vinylpyridine) and end‐sulfonic acid polystyrene and polyisoprene: Intermediates to noncovalently bonded block copolymer‐like micelles

The complexation between narrow molecular weight distribution poly(2‐vinylpyridine) (P2VP) and polystyrene (suPS) or polyisoprene (suPI) end‐functionalized with one sulfonic acid group was examined in tetrahydrofuran dilute solutions by a combination of static and dynamic laser light scattering. Both apparent weight‐average molecular weight (Mw,app) and hydrodynamic radius (Rh) of the complexes exhibited a maximum at a certain molar ratio of suPS chains to P2VP monomeric units. This indicated that the P2VP backbone may be saturated by the grafted end‐functionalized chains because of repulsion between the grafted chains. By changing the molar mass of P2VP from 100,000 to 30,000 g/mol, the values of Mw,app and Rh decreased. When suPI was used instead of suPS, similar trends were observed. In the latter case, it was possible to prepare block copolymer‐like micelles by transferring the P2VP/suPI blend solutions in decane, which is a selective solvent for PI. The non‐covalent‐bonded polymeric micelle characteristics were investigated as a function of sulfonic acid/2‐vinylpyridine units ratio as well as temperature.