Large electrostrain near the phase transition temperature of (Bi0.5Na0.5)TiO3–SrTiO3 ferroelectric ceramics

( 1 - x ) ( Bi 0.5 Na 0.5 ) Ti O 3 – x Sr Ti O 3 (abbreviated as BNST100x) was prepared by a conventional ceramic fabrication process. The depolarization temperature Td, rhombohedral-tetragonal phase transition temperature TR-T, and the temperature Tm of the maximum dielectric constant were determined from the temperature dependence of the dielectric and piezoelectric properties. It is revealed that BNST100x forms a morphotropic phase boundary of rhombohedral ferroelectric and pseudocubic (tetragonal) paraelectric at x=0.26–0.28 for BNST100x, and a very large strain and normalized strain d33* of 0.29% and 488pm∕V, respectively, were obtained at x=0.28. In addition, it was clarified that the intermediate phase between TR-T (⩾Td) and Tm shows relaxor behavior.