Effect of dispersion state of Cloisite15A® on the performance of SPEEK/Cloisite15A nanocomposite membrane for DMFC application

The introduction of 2,4,6‐triaminopyrimidine (TAP) into sulfonated poly(ether ether ketone) (SPEEK)/Cloisite15A® nanocomposite membranes were investigated for the purpose of maintaining low methanol permeability and suppressing swelling in direct methanol fuel cell (DMFC). SPEEK with 63% of degree of sulfonation (DS) was prepared by sulfonation of PEEK. Cloisite15A (7.5 wt %) along with various weight loading of TAP was incorporated into SPEEK matrix via solution intercalation method. The effect of TAP loading on the SPEEK/Cloisite15A/TAP morphology was studied. The beneficial impact of the SPEEK/Cloisite15A/TAP morphology on the physicochemical properties of the membrane was further discussed. Swelling behavior, ion exchange capacity (IEC), proton conductivity, and methanol permeability of the resultant membranes were determined as a function of Cloisite15A and TAP loadings. Uniform distribution of Cloisite15A particles in the SPEEK polymer matrix in the homogenous SPEEK/Cloisite15A/TAP nanocomposite membranes was confirmed by scanning electron microscopy and X‐ray diffraction. The water uptake of the SPEEK nanocomposite membranes decreased dramatically in the presence of TAP. The significant selectivity of SP/7.5/7.5 nanocomposite membranes could indicate a potential feasibility as a promising electrolyte for DMFC.