Comparison of quasicrystalline (T2) and crystalline (R) structures in AlCuLi using high-resolution X-ray diffraction

A high-resolution X-ray scattering experiment has been performed on quasicrystalline (T2) and crystalline (R) phases of AlCuLi alloys. Peak widths determined from the diffraction profile of the R phase are found to scale with momentum transfer G, similar to the strain-broadening effect seen in conventional crystals with small unit cells. A narrowing of peak widths on annealing is also observed. On the other hand, diffraction peak widths in I-phase samples obtained by rapid solidification are found to scale with phason momentum G 1, similar to that observed in large faceted crystals. Thermal annealing of the I phase is found to have no effect on peak widths. Our findings are discussed in the light of models for crystals and quasicrystals.