PROXIMITY EFFECTS AND CURIE TEMPERATURE ENHANCEMENT IN Co/EuS AND Fe/EuS MULTILAYERS

Two identical Co/EuS and Fe/EuS multilayers of six periods each and with individual layers of about 4 nm thick are grown by e-beam evaporation under ultrahigh vacuum conditions. The films show polycrystalline structure with a grain size limited by the individual layer thickness. Both multilayers consist of almost continuous layers with some roughness. The surface peak-to-peak roughness is about 4–5 nm. Magnetization measurements and calculations of the loops based on a Stoner–Wohlfarth-like model allow us to determine the direct antiferromagnetic exchange coupling constant between the 3d metal and EuS at 5 K. Both samples show strong enhancement of the Curie temperature of EuS up to at least 50 K with a EuS magnetization tail, which persists up to about 100 K. The J = 7/2 character of the EuS layers is shown to be responsible for the large Curie temperature enhancement.