Dislocation mobility and work hardening in sodium chloride

Stress relaxation has been used in an indirect determination of the velocity—stress exponent for dislocation motion in NaCl at room temperature. The long-range internal stress arising from plastic deformation has been estimated and it is shown to be the principal source of hardening in both stage I and stage II of plastic deformation.