Syntheses and properties of organosoluble polyamides and polyimides based on the diamine 3,3-bis[4-(4-aminophenoxy)-3-methylphenyl]phthalide derived fromo-cresolphthalein

Diamine 3,3-bis[4-(4-aminophenoxy)-3-methylphenyl]phthalide (BAMP) was derived from the o-cresolphthalein, and then it was polycondensated with various aromatic dicarboxylic acids and dianhydrides to synthesize polyamides (PAs) and polyimides (PIs), respectively. PAs have inherent viscosities of 0.78–2.24 dL/g. Most of the PAs are readily soluble in a variety of solvents such as DMF, DMAc, and NMP and afforded transparent and tough films from DMAc solutions. The cast films have tensile strengths of 75–113 MPa as well as initial moduli of 1.71–2.97 GPa. These PAs have glass transition temperatures (Tgs) in the range of 242–325°C, 10% weight loss temperatures occur up to 473°C, and char yields are between 57 and 64% at 800°C in nitrogen. PIs were first synthesized to form polyamic acids (PAAs) by a two-stage procedure that included a ring-opening reaction, followed by thermal or chemical conversion to polyimides. Inherent viscosities of PAAs are between 0.71 and 1.63 dL/g. Most of the PIs obtained through the chemical cyclodehydration procedure are soluble in NMP, o-chlorophenol, m-cresol, etc., and they have inherent viscosities of 0.58–1.32 dL/g. Tgs of these PIs are in the range of 270–305°C and show 10% weight loss temperatures up to 477°C. PIs obtained through the thermal cyclodehydration procedure have tensile strengths of 72–142 MPa, elongations at break of 8–19%, and initial moduli of 1.80–2.72 GPa.