Synthesis and application of RuSe 2 + δ nanotubes as a methanol tolerant electrocatalyst for the oxygen reduction reaction

This is the authors' abstract. We don't add key points for this paper.

This article describes an electrochemical study on the use of RuSe2 + δnanotubes as a catalyst for the oxygen reduction reaction (ORR). Uniform RuSe2 + δnanotubes were synthesized via a facile template-engaged reaction between Ru(acac)3 and t-Se nanowires at 80 °C, followed by selective removal of the unreacted t-Se cores. The resultant RuSe2 + δnanotubes were ∼55 nm in outer diameter, together with a wall thickness of ∼9 nm. These nanotubes were active for ORR and displayed high tolerance to 0.1 M methanol. While the mass-specific ORR activities at 0.7 V were ∼30 times lower than those reported for commercial Pt/C (TKK) catalysts, no detrimental effect over the ORR activity was observed upon the addition of 0.1 M methanol. In the presence of 0.1 M methanol, the mass-specific ORR activity for RuSe2 + δ was ∼12 times lower than that for Pt/C (TKK) at 0.7 V. Durability tests by chronoamperometry showed that 0.1 M methanol led to significant performance loss for Pt/C (TKK), while RuSe2 + δ was completely tolerant to 0.1 M methanol even after 1,800 s of operation.