Spatter formation is a major issue at welding speeds above 8 m/min for full penetration laser beam welding of high-alloyed steels. In experiments using a local gas flow directed at the keyhole rear wall, a reduction in spatter formation on the specimen top side was observed for welding of AISI 304. However, the interaction between gas flow and keyhole behavior with respect to the mechanisms and locations of spatter detachment, especially on the bottom side, is not yet fully understood. High-speed synchrotron X-ray imaging enables detailed insights into the keyhole behavior and the spatter formation to obtain a deeper understanding of the underlying mechanisms. During the reference experiments welding without shielding gas flow, the spatter detach from a melt pool swelling behind the keyhole aperture on both sides of the sheet. A gas flow with a low flow rate of 4.8 L/min reduces the spatter formation on the top side and the keyhole length due to the absence of oxygen affecting the surface tension. A swelling also forms on the keyhole front on the bottom side and small spatter detach undirected. Increasing the flow rate to 12.8 L/min elongates the keyhole, particularly on the specimen top side. The increased momentum transfer of the gas flow results in a periodic keyhole oscillation on the specimen top side. In combination with an elongated melt pool, the oscillation is directly correlated with the hump formation, caused by melt being pushed over the already solidified weld seam. In addition, spatter does not detach from the top side due to the changed melt flow and only detach from the keyhole front on the bottom side.
No takes yet. Share an insight, caveat, or question.
Diegel et al. (2025) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: