Influence of polymer matrix and adsorption onto silica materials on the migration ofα-tocopherol into 95% ethanol from active packaging

In this study, the effect of polymer materials with different polarity, namely low density polyethylene (LDPE) and ethylene vinyl acetate (EVA), on the migration behaviour of alpha-tocopherol from active packaging was investigated. The antioxidant was also adsorbed onto silica materials, namely SBA-15 (Santa Barbara-15) and Syloblock, in order to protect the antioxidant during extrusion and to ensure a controlled and sufficient release during the shelf-life of the food product. Migration experiments were performed at 7.0 +/- 0.5 degrees C and 95% ethanol was used as fatty food simulant. All films contained a high concentration of alpha-tocopherol, approximately 2000 mg kg(-1), to obtain an active packaging. Polymer matrix had a small influence on the migration profile. The migration of 80% of total migrated amount of antioxidant was retarded for 2.4 days by using LDPE instead of EVA. When alpha-tocopherol was adsorbed onto both silica materials, the migration of 80% of total migrated amount of antioxidant was retarded for 3.4 days in comparison to pure alpha-tocopherol. No difference was seen between the migration profiles of alpha-tocopherol adsorbed onto both silica materials. In the case of pure alpha-tocopherol, 82% of the initial amount of alpha-tocopherol in the film migrated into the food simulant at a rather fast migration rate. In the case of adsorption on silica materials, a total migration was observed. These antioxidative films can have positive food applications.