Lasing action and optical amplification in Nd^3+ doped electrooptic lanthanum lead zirconate titanate ceramics

Both single-pass gain and lasing action at 1064.4 nm were observed in ceramic gain media of neodymium doped lanthanum-modified lead zirconate titanate, which exhibits good electrooptic (EO) effect from visible through mid-wave IR band (400 nm to 5.5 µm). These works have removed roadblocks off the way leading to development of long envisioned multifunctional optical devices. The impact of the Nd3+ doping concentration on the EO effect in the Nd3+:PLZT ceramics was studied. The finding of the slowly trailing-off was satisfactorily explained with the rich vacancy-based carrier traps, which are responsible for the long persistent optoenergy storage.