Using first-principles band-structure calculations we have studied the valence-band alignment of InAs/InSb, deducing also the offset at the InAs_1-x{Sb}ₓ$/${InAs}_{1{{-}}y}Sby heterostructure. We find the following: (i) Pure InAs/InSb has a ``type-II broken gap'' alignment both with and without strain. (ii) For Sb-rich InAs_1-x{Sb}ₓ$/InSb heterostructures, the unstrained band alignment is type II; both epitaxial strain and CuPt ordering enhance the type-II character in this Sb-rich limit. (iii) For As-rich InAs/${InAs}_{1{{-}}x}Sbₓ heterostructures the top of the valence band is always on the alloy layer while the conduction-band minimum can be localized either on the alloy layer (type-I) or on the InAs layer (type-II), depending on the balance between concentration, strain, and degree of ordering/phase separation. In this case, epitaxial strain enhances the type-II character, while ordering enhances the type-I character. Our results are compared with recent experimental observations. We find that the type-I behavior noted for some As-rich InAs/InAs_1-x{Sb}ₓ$ interfaces and the type-II behavior noted in other such samples could be explained in terms of the dominance of ordering and strain effects, respectively.
No takes yet. Share an insight, caveat, or question.
Wei et al. (1995) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: