Free‐volume properties, size and distribution, in amorphous polystyrene exposed to CO2 gases have been measured as a function of pressure to 800 psi (5.5 MPa), of time, and of temperature using positron annihilation lifetime spectroscopy. The free volume increases significantly and its distribution broadens as a function of pressure. The free volume relaxes as a function of time with a characteristic time of 15 h, and 5.7 h for 400, and 800 psi, respectively, after depressurizing under vacuum. A portion of free volume created by CO2 exposure remains permanently in the polymer after CO2 exposure. The glass transition temperature decreases significantly as a function of CO2 pressure from the free‐volume data and is compared with the differential scanning calorimeter results. The observed free‐volume variations as a function of pressure, time, and temperature are discussed in terms of hole expansion, creation, free‐volume relaxation, plasticization, and hole filling in amorphous polymers.
No takes yet. Share an insight, caveat, or question.
Chen et al. (2007) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: