A Simple Route to Fabricate Percolated Perpendicular Magnetic Recording Media

A simple approach is proposed for fabrication of percolated perpendicular media (PPM). Nano pore array with pore diameter of 12-15 nm and different pore densities has been prepared by anodizing aluminum on silicon wafers. The pore density increases from 3.2times1010cm-2to 11.0times1010cm-2with the decrease in anodizing voltage from 30 to 10 V. Then, Pt (7 nm)/{Co (0.5 nm)/Pt (2) nm}5multilayers are deposited onto this porous anodized alumina (AAO) by sputtering. The pore size is reduced to 10-12 nm after deposition of magnetic layers. The Co/Pt multilayers on AAO exhibit perpendicular magnetic anisotropy, squareness ratios of unity, and negative nucleation fields. The perpendicular coercivity increases linearly with the increase in pore density due to the pinning effect imposed by the pores, which is consistent with theoretical calculation for PPM