Transport and magnetic properties of Fe doped CaMnO3

The structural, transport, and magnetic properties of CaMn1−xFexO3−δ (0.0 ≤ x ≤ 0.3) have been studied by using resistivity, magnetization, and neutron powder diffraction techniques. The compounds are found to be isostructural and crystallize in GdFeO3-type orthorhombic structure (space group Pnma). With Fe doping, no structural change is observed. Mössbauer and paramagnetic susceptibility measurements show that Fe substitutes in 4+ valence state, and XANES measurements indicate the presence of mixed valence state of Mn. The compounds exhibit insulating behavior in the studied temperature range. The temperature dependence of resistivity is found to be described by small polaron model for x = 0 and variable range hopping model for x = 0.1. For higher x values, it follows a parallel combination resistance model. A small reduction in TN from 120 K to 100 K with increase in x is found. The magnetic structure changes from Gz-type collinear antiferromagnetic (AFM) structure for x = 0.0 to canted AFM structure GZFY-type for Fe doped compounds. The AFM component of the moment progressively decreases with x while FM component exhibits a maximum at x = 0.2.