Fluctuation microscopy studies of medium-range ordering in amorphous diamond-like carbon films

In this letter, we report fluctuation microscopy studies of medium-range ordering in amorphous diamond-like carbon films and the effect of annealing on this ordering. Annealed and unannealed diamond-like carbon films have almost identical short-range order. Our fluctuation microscopy results, however, indicate the presence of medium range order or clustering in the films on a lateral length scale that exceeds 1 nm. Within the clustered regions, the dominant local ordering appears to be diamond-like, and graphite-like ordering is not observed. Thermal annealing up to 600 °C leads to an increase in diamond-like clustering with no onset of graphite-like clustering. However, after high temperature annealing up to 1000 °C, graphite-like clustering becomes apparent as a result of the conversion of diamond-like carbon to graphite-like carbon. The results on the as-deposited films and films annealed up to 600 °C suggest that a spontaneous medium range ordering process occurs in diamond-like carbon films during and subsequent to film growth, and this may play an important role in stress relaxation.