Room temperature photoluminescence from nanostructured amorphous carbon

Visible room-temperature photoluminescence (PL) was observed from hydrogen-free nanostructured amorphous carbon films deposited by pulsed laser ablation in different background pressures of argon (PAr). By varying PAr from 5to340mTorr, the film morphology changed from smooth to rough and at the highest pressures, low-density filamentary growth was observed. Over the same pressure regime an increase in the ordering of sp2 bonded C content was observed using visible Raman spectroscopy. The origin of the PL is discussed in terms of improved carrier localization within an increased sp2 rich phase.