Mechanical Effects of Off-Axis Insertion of Locking Screws

OBJECTIVES: The purposes of this study were to evaluate the cantilevered bending strength and failure modes of locking screws inserted at various angles in a plate with fully circumferential threaded holes. As an additional measure, the amount of screw head prominence at these angles was also assessed. METHODS: Standard 3.5-mm locking screws were inserted into round fully circumferential threaded holes through a standard straight 3.5-mm locking plate at various angles. The achieved angle of insertion and its prominence protruding from the far-bone side of the plate was measured using an optical luminescence technique. Each screw was then loaded at a constant rate until failure in a cantilevered bending scenario. The maximum cantilevered bending strength was measured, and the moment at failure was calculated. RESULTS: There was a positive correlation between increasing insertion angle and increasing prominence; a higher screw insertion angle yielded greater prominence. Prominence values ranged from negligible to 2 mm. As screw insertion angle increased, the bending moment at failure decreased. Screws inserted to 3 degrees or below primarily failed through screw deformation at the minor diameter below the head, whereas screws inserted to greater than 3 degrees primarily failed through locking mechanism disengagement. CONCLUSIONS: These findings indicate that cross threading may not be biomechanically advantageous and may change screw mode of failure. Based on these findings, screws inserted to 3 degrees or higher would reduce the bending moment at failure to approximately 50% of an orthogonally inserted screw.