Preparation and characterization of exfoliated layered double hydroxide/silicone rubber nanocomposites

Silicone rubber (SR)/Mg–Al layered double hydroxide (LDH) nanocomposites were prepared by the solution intercalation of SR crosslinked by a platinum‐catalyzed hydrosilylation reaction into the galleries of dodecyl sulfate intercalated layered double hydroxide (DS–LDH). X‐ray diffraction and transmission electron microscopy analysis showed the formation of exfoliated structures of organomodified LDH layers in the SR matrix. The tensile strength and elongation at break of SR/DS–LDH (5 wt %) were maximally improved by 53 and 38%, respectively, in comparison with those of the neat polymer. Thermogravimetric analysis indicated that the thermal degradation temperature of the exfoliated SR/DS–LDH (1 wt %) nanocomposites at 50% weight loss was 20°C higher than that of pure SR. Differential scanning calorimetry analysis data confirmed that the melting temperature of the nanocomposites increased at lower filler loadings (1, 3, and 5 wt %), whereas it decreased at a higher filler loading (8 wt %). The relative improvements in the solvent‐uptake resistance behavior of the SR/DS–LDH nanocomposites were also observed.