Bioinspired Peptide-Coated Superhydrophilic Poly(vinylidene fluoride) Membrane for Oil/Water Emulsion Separation

Polyvinylidene fluoride (PVDF) membranes are limited in the field of oil-in-water emulsion treatment because the intrinsic hydrophobicity of PVDF can cause serious membrane fouling. Here, a superhydrophilic PVDF membrane (PVDF@PDA-GSH) was fabricated using a facile, versatile, mussel-inspired method. The pristine PVDF membrane was coated with dopamine under mild alkaline conditions by a dip-coating method, followed by addition of glutathione (GSH) via a simple reaction. GSH was successfully coated onto the membrane surface and confirmed by X-ray photoelectron spectroscopy and energy dispersive X-ray spectrometry. Hierarchical surface structure and superhydrophilicity were examined by scanning electron microscopy and contact angle, respectively, giving the PVDF@PDA-GSH membrane excellent wettability and antifouling ability. The water flux of PVDF@PDA-GSH was several-fold higher than conventional filtration membranes, and the oil rejection ratio was nearly 99%. The PVDF@PDA-GSH membrane also showed favorable reusability because the flux recovery ratio (FRR) remained above 90% after five cycles. In general, these results indicated that this modification might provide a good method for the fabrication of superhydrophilic PVDF membranes with good prospects for water filtration applications.