It is shown that Ca2+ doping at Bi-site results in the release of weak ferromagnetism in BiFeO3. Structural transformation from rhombohedral to triclinic is observed with 10% Ca doping. Raman measurements show the presence of oxygen vacancies with Ca doping and no evidence of either intermediate valence or the tetravalence of iron is observed from Mössbauer measurements. No significant change in Neel temperature is observed with Ca doping. The observed weak ferromagnetism and ferroelectric nature at room temperature indicates the multiferroic nature of Bi1−xCaxFeO3 (x=5% and 10%) samples.