Influence of Chemical Composition and Microstructural Transformation of Two Low-Carbon Steels on Fine Blanking and Further Carbonitriding Heat Treatment

The effect of the chemical composition of two low-carbon steels, C18E and 22MnB5, on their behavior after forming by fine blanking was investigated. A specific tool, adaptable to a tensile testing machine, was designed to replicate an industrial half-cutting process. This tool allows for the production of samples with simple geometries and easy modification of the processing conditions. Residual elements in the raw material, concentrated in segregation bands, appear to play a key role in crack initiation within the shear zone during the blanking process. The role of non-metallic inclusions is discussed to explain the presence of large cracks in C18E, while 22MnB5 only shows damage nucleation. After fine blanking, a carbonitriding heat treatment process was performed to modify the initial microstructure and achieve the required mechanical properties in the final parts. Continuous cooling transformation diagrams were created for both steels to guide this process. The results of this study demonstrate the better formability of 22MnB5 by fine blanking, compared to that of C18E.