Experimental study demonstrates comparable texturability between recycled bottle and virgin polymer yarns, indicating recycled plastic can reliably replace raw supplies in textile manufacturing.
In the present work, the texturability of filament yarns produced from recycled bottle grade polyethylene terephthalate (R-PET) and new fiber grade PET (FG-PET) were investigated and compared experimentally. Yarn spun on a spin-draw spinning machine was draw-textured. Elongation at break in each fiber was set to reach 30 ± 5% in the texturing machine. The effect of the draw-texturing conditions on thermomechanical, structural, and crimp properties were examined. Draw-texturing behaviors of the fibers were analyzed using differential scanning calorimetry and measurements of intrinsic viscosity, mechanical and crimp properties, density, and X-ray diffraction. The results indicate that crystallinity of the textured yarn from R- PET and FG-PET has increased compared to the semi-drawn yarns. Further, the lateral dimensions of the R-PET crystals are relatively well developed. Crimp properties show nearly similar response for two polymer yarns for the texturing process. It was found that R-PET can be the premier feed supply for the draw-texturing process and that filaments with appropriate confidence could be obtained from the R-PET.
No takes yet. Share an insight, caveat, or question.
Abbasi et al. (2020) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: