Pt-Functionalized PdO Nanowires for Room Temperature Hydrogen Gas Sensors

In this work, we prepared a well-aligned palladium oxide nanowire (PdO NW) array using the lithographically patterned Pd nanowire electrodeposition (LPNE) method followed by subsequent calcination at 500 °C. Sensitization with platinum (Pt) nanoparticles (NPs), which were functionalized on PdO NWs through a simple reduction process, significantly enhanced the detection capability of the Pt-loaded PdO NWs (Pt-PdO NWs) sensors toward hydrogen gas (H 2 ) at room temperature. The well-distributed Pt NPs, which are known chemical sensitizers, activated the dissociation of H 2 and oxygen molecules through the spillover effect with subsequent diffusion of these products to the PdO surface, thereby transforming the entire surface of the PdO NWs into reaction sites for H 2 . As a result, at a high concentration of H 2 (0.2%), the Pt-PdO NWs showed an enhanced sensitivity of 62% (defined as Δ R / R air × 100%) compared to that (6.1%) of pristine PdO NWs. The Pt-PdO NWs exhibited a response time of 166 s, which was 2.68-fold faster than that of pristine PdO NWs (445 s). In addition, the Pt-PdO NWs responded to a very low concentration of H 2 (10 ppm) with a sensitivity of 14%, unlike the pristine PdO NWs, which did not exhibit any response at that concentration. These outstanding results are mainly attributed to a homogeneous decoration of Pt NPs on the surface of well-aligned PdO NWs. In this work, we demonstrated the potential suitability of Pt-PdO NWs as a highly sensitive H 2 sensing layer at room temperature.