Room temperature mid-infrared fiber lasing beyond 5 µm in chalcogenide glass small-core step index fiber

This Letter, to the best of our knowledge, reports mid-infrared fiber lasing beyond 5 µm at room temperature for the first time, C e 3 + -doped, chalcogenide glass, step index fiber employed in-band pumping with a 4.15 µm quantum cascade laser. The lasing fiber is was 64 mm long, with a calculated numerical aperture of 0.48 at the lasing wavelengths. The core glass was G e 15 A s 21 G a 1 S e 63 atomic % (at. %), doped with 500 parts-per-million-by-weight Ce, with a 9 µm core diameter. The cladding glass was G e 21 S b 10 S e 69 at. % with a 190 µm outer diameter. As pump power increases continuous wave lasing corresponding to the 2 F 7 / 2 → 2 F 5 / 2 , transition in the C e 3 + ion occurs at 5.14 µm, 5.17 µm, and 5.28 µm.