Nanotube Array-Like WO3 Photoanode with Dual-Layer Oxygen-Evolution Cocatalysts for Photoelectrocatalytic Overall Water Splitting

This is the authors' abstract. We don't add key points for this paper.

The nanotube array-like WO 3 (WA) photoanode has been widely utilized in solar-driven photoelectrocatalytic applications due to its excellent light absorption. However, it still suffers from a low quantum efficiency. Herein, double oxygen-evolution catalyst (OEC) layers (FeOOH and NiOOH) were deposited onto the surface of WA with the formation of a WA-FeOOH/NiOOH photoanode (WA-FeNi). The FeOOH greatly decreased the WA/OEC interfacial electron–hole pair recombination rate, while the NiOOH reduced the OEC/electrolyte interfacial electron–hole pairs recombination and promoted the composite’s water oxidation activity significantly. The as-formed WA-FeNi photoanode possessed a photocurrent density of 120 μA/cm 2 under simulated sunlight irradiation, which is almost 200% that of WA. The electron–hole separation yield at 0.6 V versus SCE in the former was determined to be 39.3%, which is nearly 2.5 times that of the latter. As a result, the photoanode exhibited superstrong simulated-sunlight-driven photoelectrocatalytic overall water splitting, with a H 2 evolution rate of 3.43 μmol cm –2 h –1 . This research provides an effective method for constructing a highly active WO 3 -based photoelectrocatalytic system for overall water splitting.