Reversible hysteresis inversion in MoS2 field effect transistors

The origin of threshold voltage instability with gate voltage in MoS 2 transistors is poorly understood but critical for device reliability and performance. Reversibility of the temperature dependence of hysteresis and its inversion with temperature in MoS 2 transistors has not been demonstrated. In this work, we delineate two independent mechanisms responsible for thermally assisted hysteresis inversion in gate transfer characteristics of contact resistance-independent multilayer MoS 2 transistors. Variable temperature hysteresis measurements were performed on gated four-terminal van der Pauw and two-terminal devices of MoS 2 on SiO 2 . Additional hysteresis measurements on suspended (~100 nm air gap between MoS 2 and SiO 2 ) transistors and under different ambient conditions (vacuum/nitrogen) were used to further isolate the mechanisms. Clockwise hysteresis at room temperature (300 K) that decreases with increasing temperature is shown to result from intrinsic defects/traps in MoS 2 . At higher temperatures a second, independent mechanism of charge trapping and de-trapping between the oxide and p + Si gate leads to hysteresis collapse at ~350 K and anti-clockwise hysteresis (inversion) for temperatures >350 K. The intrinsic-oxide trap model has been corroborated through device simulations. Further, pulsed current–voltage ( I – V ) measurements were carried out to extract the trap time constants at different temperatures. Non-volatile memory and temperature sensor applications exploiting temperature dependent hysteresis inversion and its reversibility in MoS 2 transistors have also been demonstrated.