Influence of in-situ annealing ambient on p-type conduction in dual ion beam sputtered Sb-doped ZnO thin films

Sb-doped ZnO (SZO) films were deposited on c-plane sapphire substrates by dual ion beam sputtering deposition system and subsequently annealed in-situ in vacuum and in various proportions of O2/(O2 + N2)% from 0% (N2) to 100% (O2). Hall measurements established all SZO films were p-type, as was also confirmed by typical diode-like rectifying current-voltage characteristics from p-ZnO/n-ZnO homojunction. SZO films annealed in O2 ambient exhibited higher hole concentration as compared with films annealed in vacuum or N2 ambient. X-ray photoelectron spectroscopic analysis confirmed that Sb5+ states were more preferable in comparison to Sb3+ states for acceptor-like SbZn-2VZn complex formation in SZO films.