Flexible nanocrystalline‐titania/polyimide hybrids with high refractive index and excellent thermal dimensional stability

In this study, a novel synthetic route was developed to prepare polyimide–nanocrystalline–titania hybrid optical films with a relatively high titania content (up to 50 wt %) and thickness (20–30 μm) from soluble polyimides containing hydroxyl groups. Two series of newly soluble polyimides were synthesized from the hydroxy‐substituted diamines with various commercial tetracarboxylic dianhydrides. The hydroxyl groups on the backbone of the polyimides could provide the organic–inorganic bonding and resulted in homogeneous hybrid solutions by controlling the mole ratio of titanium butoxide/hydroxyl group. AFM, SEM, TEM, and XRD results indicated the formation of well‐dispersed nanocrystalline‐titania. The flexible hybrid films could be successfully obtained and revealed relatively good surface planarity, thermal dimensional stability, tunable refractive index, and high optical transparency. A three‐layer antireflection coating based on the hybrid films was prepared and showed a reflectance of less than 0.5% in the visible range indicated its potential optical applications.