Differential scanning calorimetry study on thermal behaviors of freeze‐dried poly(L‐lactide) from dilute solutions

Glass transition, cold crystallization, and melting of freeze‐dried poly(L‐lactide) (PLLA) prepared from dilute 1,4‐dioxane solutions were investigated by differential scanning calorimetry (DSC). Conventional DSC measurements of heating scans revealed that freeze‐dried PLLA prepared from a 0.07 wt % solution undergoes a two‐step cold crystallization (or reorganization) with a lower exotherm appearing at about 78 °C and with a higher broad exotherm between 110–155 °C. The peak temperature of the former exotherm is about 50 K lower than that observed for a reference bulk sample. Step‐scan mode DSC, which provides information essentially equivalent to that obtained from the temperature‐modulated DSC, revealed that the glass‐transition temperature is about 6 K lower than that of the reference bulk. These findings suggest enhanced chain mobility for freeze‐dried PLLA. Freeze‐dried PLLA that crystallized at 80 °C for 40 min was revealed to contain a rather large amount of rigid amorphous material (42%).