[Co/Ni]-CoFeB hybrid free layer stack materials for high density magnetic random access memory applications

Alternative free layer materials with high perpendicular anisotropy are researched to provide spin-transfer-torque magnetic random access memory stacks' sufficient thermal stability at critical dimensions of 20 nm and below. We demonstrate a high tunnel magetoresistance (TMR) MgO-based magnetic tunnel junction stack with a hybrid free layer design made of a [Co/Ni] multilayer and CoFeB. The seed material on which the [Co/Ni] multilayer is deposited determines its switching characteristics. When deposited on a Pt seed layer, soft magnetic switching behavior with high squareness is obtained. When deposited on a NiCr seed, the perpendicular anisotropy remains high, but the squareness is low and coercivity exceeds 1000 Oe. Interdiffusion of the seed material with the [Co/Ni] multilayers is found to be responsible for the different switching characteristics. In optimized stacks, a TMR of 165% and low resistance-area (RA) product of 7.0 Ω μm2 are attained for free layers with an effective perpendicular magnetic anisotropy energy of 1.25 erg/cm2, which suggests that the hybrid free layer materials may be a viable candidate for high density magnetic random access memory applications.