Living radical polymerization. II. Improved atom transfer radical polymerization of acrylamide in aqueous glycerol media with a novel pentamethyldiethylenetriamine‐based soluble copper(I) complex catalyst system

An improved atom transfer radical polymerization (ATRP) of acrylamide was achieved in a glycerol/water (1:1 v/v) medium with 2‐halopropionamide initiators, CuX (X = Cl or Br) as catalysts, pentamethyldiethylenetriamine (PMDETA) as a ligand, and CuX2 (≥20 mol % CuX) and excess alkali halide (ca. 1 mol/dm3) as additives. The first‐order kinetic plots for the disappearance of the monomer at 130 °C were linear; this was a significant improvement over the results obtained earlier with the bipyridine ligand. However, even under such improved situations, about 7 mol % of the polymer chains were estimated to be formed dead. The polydispersity index was approximately 1.5. At a lower temperature (ca. 90 °C), a lower polydispersity index (1.24) was obtained for the bromide‐based initiating system. Chain‐extension experiments proved the living nature of the polymers. The presence of both extra halide ions and the monomer was necessary to take the CuX–PMDETA complex into solution. It was suggested that the soluble Cu(I) complex was formed with one PMDETA molecule acting as a monodentate ligand and with two halide ions and one acrylamide molecule occupying the other three coordination sites. Some support for the involvement of all three ligands (X−, PMDETA, and acrylamide) in the complex formation was obtained from ultraviolet–visible spectroscopy studies. The better ATRP with the PMDETA ligand was attributed to the better stability and lesser hydrolysis of the 1:1 Cu+2/PMDETA complex with respect the corresponding bipyridine complex.