In vitro study reveals sub-mol% silver oxide enhances network connectivity and durability in aluminoborophosphate glasses without antibacterial efficacy, indicating higher dopant levels are required.
The influence of low-level (0.25–0.75 mol%) silver oxide (Ag 2 O) substitution for Na 2 O on glass structure and in vitro dissolution of sodium–calcium aluminoborophosphate glasses was investigated. Spectroscopic analysis showed that the borate sub-network is dominated by BO 4 units (>78%), whereas the phosphate sub-network contains mainly Q 1 species with an increasing contribution of Q 2 environments at higher Ag 2 O content, accompanied by Al 2 O 3 enrichment. These changes are consistent with increased network connectivity, including a higher contribution of more polymerized phosphate environments and changes in mixed B–O–P-related environments. In vitro dissolution tests showed that the glass with 0.75 mol% Ag 2 O exhibited lower mass loss and more pronounced pH increase than the lower-Ag and Al compositions. These trends are consistent with a more connected and chemically durable borophosphate network. After immersion, EDX, XRD, and FTIR confirmed the formation of calcium-phosphate-rich surface deposits, mainly apatite-like in character. No measurable antibacterial activity against E. coli and MRSA was observed under the applied test conditions. The results indicate that sub-mol% Ag 2 O substitution is associated with measurable changes in the structure and reactivity of sodium–calcium aluminoborophosphate glasses, but at the investigated concentrations it does not provide measurable antibacterial functionality.
No takes yet. Share an insight, caveat, or question.
Bonalska et al. (2026) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context:
More from Materials Chemistry and Physics