Role of Zr4+ Cations in NO2 Adsorption on Ce1-xZrxO2 Mixed Oxides at Ambient Conditions

Mixed oxides Ce(1-x)Zr(x)O(2) prepared by slow coprecipitation in NaOH were tested for NO(2) adsorption in dynamic conditions at room temperature. The samples were characterized before and after exposure to NO(2) by XRD, N(2)-adsorption, thermal analysis, potentiometric titration, and FT-IR. Mixed oxides show a better NO(2) adsorption capacity than the parent materials (CeO(2) and Zr(OH)(4)). This effect is linked to the presence of reduced cerium and oxygen vacancies induced by the addition of Zr(4+) cations to the structure. The results indicate that NO(2) reacts with Ce(3+) to form nitrite and nitrate species on the surface. The NO retention increases with an increase in the Zr(OH)(4) content. A decrease in the density of -OH groups on the surface after the exposure to NO(2), suggests their involvement in reactive adsorption of NO and/or NO(2). From the structural point of view, no real difference was observed on the Ce(1-x)Zr(x)O(2) materials before and after exposure to NO(2).