The cellulose paper treated in proportional mixture systems showed higher liquid absorption compare to only EtOH and MeOH treatments. It was approximately 40-70% and 50-91% higher for EtOH-NaOH and MeOH-NaOH treated papers, respectively. All conditions apparently bring about an effect of decreased strength for papers. The lowest tensile strength of 13.0 N/mm was found with EtOH and NaOH treated samples after 5(th) repeating wetting-drying stage. But, some conditions gave approximately 21-59.5% higher stretch than untreated samples. The pore size distributions of papers were evaluated with Simons stain procedure and experimental results usually consisted with sorption data. The less intense CH(2)-CH(2)- vibrations (1450-1700 cm(-1)) and C-C and C-O-C peak areas in FTIR spectra indicates lowering H-bonds in solvent treated and dried paper network structure.
No takes yet. Share an insight, caveat, or question.
Şahin et al. (2008) studied this question.
Synapse has enriched 5 related papers. Consider them for comparative context: