Facile Synthesis of Manganese‐Loaded Mesoporous Silica Materials by Direct Reaction Between KMnO4 and an In‐Situ Surfactant Template

A series of manganese oxide‐loaded SBA‐15 (MnSBA‐xh, x = 1, 2, 3, 4, 5, 6; h: hour(s)) mesoporous materials are synthesized via a facile, in‐situ reduction method with a surfactant template. The composite materials are characterized using Fourier‐transform infrared spectroscopy, X‐ray diffraction, N2 sorption isotherms, X‐ray photoelectron spectroscopy (XPS), transmission electron microscopy, energy‐dispersive spectroscopy, and CO oxidation catalysis. The results show that a high content of manganese (an atomic ratio of Mn/Si from 0.12 up to approximately 1) could be loaded into the channels of SBA‐15 when treated with an aqueous solution of potassium permanganate, while retaining the ordered mesostructure and large surface area of SBA‐15. Increasing the manganese oxide content results in a gradual decrease in the specific surface area, pore size, and pore volume. XPS spectra are employed to confirm the redox reaction between KMnO4 and the surfactant. CO‐conversion tests on the calcined MnSBA‐2h sample (MnSBA‐2h‐cal) shows that it has a repeatable, and relatively high, catalytic activity.