Sequential interpenetrating poly(ethylene glycol) hydrogels prepared by UV‐initiated thiol–ene coupling chemistry

Poly(ethylene glycol) (PEG)‐diallyls, ranging from 2 to 8 kDa, were successfully reacted with a trifunctional thiol crosslinker via thiol–ene coupling reaction to construct four different primary PEG hydrogels. These systems were used as scaffolds for the preparation of a library of sequential interpenetrating networks (SeqIPNs). The solid content of the secondary networks varied between 21 and 34% and was dependent on the length of the absorbing PEGs. The gel fractions for the IPNs were above 85%. Additionally, the lowest degree of swelling was found for the IPN based on 2‐kDa PEG (315%), whereas the 8‐kDa PEG IPN exhibited a value of 810%. The SeqIPN strategy facilitated hydrogel systems that cover a larger domain of tensile modulus (192–889 kPa) when compared with single hydrogel networks (175–555 kPa).