A Study on Structure and Mechanical Properties of Polyurethane/Organic-Montmorillonite Nanocomposites

The intercalated nanocomposites of polyurethane (PU) with organic-montmorillonite (OMMT) treated by cetryltrimethyl ammonium bromide was prepared. The interlayer spacing of PU/OMMT nanocomposites was 3–4 nm. The interface interaction of PU/OMMT nanocomposites was improved compared to that of PU/montmorillonite (MMT) composites. The orderly arrangement of the PU chains was hindered because of strong interface interaction between the silicate layers dispersed in the nanometer and PU chains. By adding 2 wt% OMMT to PU, tensile strength and tear strength of the PU/OMMT composites were increased from 10.5 MPa and 36.4 KN/m to 13.8 MPa and 42.2 KN/m, respectively. The tensile strength and tear strength increased with OMMT content firstly, reaching its maximum when the OMMT content was 8 wt%. After that, the tensile strength and tear strength decreased with the further increase of the OMMT content. Compared to that of PU, the elongation at break of the PU/OMMT nanocomposites increased, indicating that the stretch of PU/OMMT nanocomposites increased.