Synthesis of poly(vinylidene fluoride) (PVdF)/silica hybrids having interpenetrating polymer network structure by using crystallization between PVdF chains

High transparent and homogeneous poly(vinylidene fluoride) (PVdF)/silica hybrids were obtained by using an in‐situ interpenetrating polymer network (IPN) method. The simultaneous formation of PVdF gel resulting from the physical cross‐linking and silica gel from sol–gel process prevented the aggregation of PVdF in silica gel matrix. To form the physical cross‐linking between PVdF chains, the cosolvent system of dimethylformaide (DMF) and γ‐butyrolactone was used. The obtained PVdF/silica hybrids had an entangled combination of physical PVdF gel and silica gel, which was called a “complete‐ IPN” structure. The physical cross‐linking between PVdF chains in silica gel matrix was confirmed by differential scanning calorimetry (DSC) measurements. The miscibility between PVdF and silica phase was examined by scanning electron microscopy (SEM) and tapping mode atomic force microscopy (TM‐AFM) measurements.