Experimental evaluation of the catalytic efficiency of calcium based natural and modified catalyst for biodiesel synthesis

Transesterification of a mixture of vegetable oils with methanol using metal oxide catalysts derived from snail shell (SS) for biodiesel production was investigated. The metal oxides obtained from calcined snail shells in the temperature range of 650°–950 °C and modified by loading different potassium salts were used as a catalyst in the process. The catalysts were characterized by FT-IR, XRD, SEM-EDS, XPS and TGA. Catalytic activities of developed catalysts were also tested by Hammet indicator method and ion exchange method. The best calcination conditions were observed at 850°C for 4 hours based on biodiesel yield. The KF loaded snail shell gave highest biodiesel yield of 98 ± 1% in a batch reactor with highest basicity (15.9 mmoles/g) and basic strength measured by Hammet method. The optimized reaction conditions were: reaction temperature 65°C, reaction time 3 hours, methanol to oil molar ratio 9:1 and catalyst concentration 3wt%. Leaching and reusability tests confirm the stability of the catalyst as it encounters only 3% of leaching and small changes in catalytic activity up to five runs in terms of biodiesel yield.