Synthesis and properties of poly(tetramethylene terephthalate‐co‐ethylene terephthalate)–poly(tetramethylene ether) segmented copolymers

A series of polyether–copolyester segmented copolymers ((PBT–PET)PTMG) based on hard segments of tetramethylene terephthalate–ethylene terephthalate copolyester (PBT–PET) and soft segments of poly(tetramethylene ether)(PTMG) was synthesized. The hard : soft segment weight ratio was 30 : 70 and the mole ratio of PBT : PET was 1 : 10; 1 : 6; 1 : 1; 3 : 1, respectively. Their mechanical properties, morphology, crystallization behavior and optical transparency were investigated and compared with poly(tetramethylene terephthalate)–poly(tetramethylene ether)(PBT–PTMG), as well as with poly(ethylene terephthalate)–poly(tetramethylene ether)(PET–PTMG), consisting of the equivalent composition ratio of hard and soft segments. It was found that the transparency could be improved by introducing a small amount of PBT into PET–PTMG through copolymerization. However, a decrease was observed in the transparency if more PBT was added. This is due to the fact that the copolymerization makes both crystallinity and crystallization rate decrease.