Synthesis of UV‐curable hyperbranched polyurethane (meth)acrylate oligomers via thiol‐ene “click” chemistry

First, the second‐generation hyperbranched poly(amine‐ester) (G2‐OH) was successfully prepared by thiol‐ene “click” chemistry. Subsequently, a series of photosensitive hyperbranched oligomers (G2‐ORs) were synthesized by facile modifications of the G2‐OH with acryloyl chloride, methacryloyl chloride, IPDI‐HEA, and IPDI‐HEMA, respectively. The structures of hyperbranched oligomers were characterized by element analysis, FT‐IR, 1H NMR, GPC and viscosity measurement. It was shown that these synthesized oligomers have narrow molecular weight distribution and low intrinsic viscosity at 30°C. UV–vis spectra results showed that the G2‐ORs had sharp absorption bands at around 202 nm. The results of photosensitivities measurement indicated that the G2‐Macr shows the highest photosensitive than other hyperbranched oligomers in the absence of photoinitiator. In addition, these UV‐cured photosensitive G2‐ORs had good thermal properties. The solubilities of the synthesized hyperbranched oligomers were also examined.