Recombination velocity less than 100 cm/s at polycrystalline Al2O3/CdSeTe interfaces

Reducing recombination in polycrystalline solar cells by orders of magnitude is currently one of the greatest challenges for increasing thin-film solar cell efficiency to theoretical limits. The question of how to do this has been a challenge for the thin-film community for decades. This work indicates that effective interface passivation is critical. Here, polycrystalline Al2O3/CdSeTe/Al2O3/glass heterostructures are grown, and a combination of spectroscopic, microscopic, and time-resolved electro-optical measurements demonstrates that the interface recombination velocity at alumina/thin-film interfaces can be less than 100 cm/s. This is three orders of magnitude less than typical CdTe interfaces without passivation, commensurate with single-crystal epitaxial CdMgSeTe/CdSeTe/CdMgSeTe double heterostructures, and enables minority-carrier lifetimes in polycrystalline CdSeTe well above 100 ns. Microscopic interfacial electric-field measurements identify the field effect as a potential mechanism for polycrystalline Al2O3/CdSeTe interface passivation. The results provide guidance for modeling and interface passivation in devices and indicate future paths to realize highly efficient thin-film solar cells.