Antiferroelectric phase transition in (Sr1-xCax)TiO3: II. X-ray diffraction studies

We present here a detailed Rietveld analysis of the structure of paraelectric and antiferroelectric phases of Sr 0.70 Ca 0.30 TiO 3 using powder XRD data. It is shown that the observed antiferroelectric superlattice reflections can be explained by doubling of the C o parameter of the orthorhombic paraelectric phase. The space groups of the paraelectric (PE) and antiferroelectric (AFE) phases are shown to be Ibnm and Pbcm respectively. The ionic displacements in the antiferroelectric phase reveal that the Ti 4+ and Sr 2+ /Ca 2+ ions are displaced in the + [100] direction in a block of three layers followed by their displacements in the -[100] direction in the next block of three layers, leading to the doubling of the cell parameter in the [001] direction. The paraelectric to antiferroelectric phase transition in (Sr 0.70 Ca 0.30 )TiO 3 and (Sr 0.75 Ca 0.25 )TiO 3 is shown to be of first order type since (i) the AFE and PE phases coexist around the phase transition temperature and (ii) the lattice parameters change discontinuously at the transition temperature.