Three-Dimensional Reconstruction and Analysis of All-Solid Li-Ion Battery Electrode Using Synchrotron Transmission X-ray Microscopy Tomography

A synchrotron transmission X-ray microscopy tomography system with a spatial resolution of 58.2 nm at the Advanced Photon Source was employed to obtain three-dimensional morphological data of all-solid Li-ion battery electrodes. The three-phase electrode was fabricated from a 47:47:6 (wt %) mixture of Li(Ni 1/3 Mn 1/3 Co 1/3 )O 2 as active material, Li 1.3 Ti 1.7 Al 0.3 (PO 4 ) 3 as Li-ion conductor, and Super-P carbon as electron conductor. The geometric analysis show that particle-based all-solid Li-ion battery has serious contact interface problem which significantly impact the Li-ion transport and intercalation reaction in the electrode, leading to low capacity, poor rate capability and cycle life.