Maraging steels are alloys with a good balance between strength and fracture toughness. These properties are obtained by quenching and aging treatments, where the precipitation of intermetallic compounds is promoted in a martensitic matrix. In this context, this paper aims to evaluate the effect of hot deformation on microstructure, kinetics and formation of reverted austenite in a C350 maraging steel modified by titanium addition, in order to improve the mechanical properties without addition of alloying elements. The following characterization techniques were used: optical microscopy (OM), Scanning Electron Microscopy (SEM) and Transmission Electron Microscopy (TEM), X-Ray Diffraction (XRD), Vickers microhardness and Dilatometry. The results showed that the deformation promoted a refinement of martensitic packages and blocks, proportional to the reduction of height and a preferred alignment towards the center of the sample. In the aging treatment, the deformation accelerated the kinetics of precipitation and formation of reverted austenite. It was also verified a reduction of the volumetric variation produced by reactions and a reduction of precipitation temperature and formation of reverted austenite in the greater deformation.
No takes yet. Share an insight, caveat, or question.
Freitas et al. (2018) studied this question.
Synapse has enriched 10 related papers. Consider them for comparative context: