Germanium-induced stabilization of a very high-k zirconia phase in ZrO2/GeO2 gate stacks

Electrical data on ZrO2/GeO2 stacks prepared by atomic oxygen beam deposition on Ge at 225 °C reveal a relatively weak dependence of the stack equivalent oxide thickness upon the ZrO2 thickness. This trend points to a very high zirconia dielectric permittivity (k) value which is estimated to be around 44. This is indicative of zirconia crystallization into a tetragonal phase which is also supported by x-ray diffraction data. X-ray photoelectron spectroscopy analysis is in line with the assumption that due to a finite GeO2 decomposition, Ge is incorporated into the growing ZrO2, thus, stabilizing the high-k tetragonal phase.