Reversible‐addition fragmentation chain transfer radical emulsion polymerization by a nanoprecipitation process

This is the authors' abstract. We don't add key points for this paper.

Polymerizations of styrene under emulsion reversible‐addition fragmentation chain transfer polymerization conditions are reported. Using a recently developed nanoprecipitaiton process, emulsion particles were formed by the precipitation of an acetone solution of a macroRAFT agent into an aqueous solution of poly(vinyl alcohol). The particles were then swollen with monomer and subsequently polymerized. Emulsion polymerizations were performed at 65 and 75 °C in which either KPS, BPO, or a combination of both was used as an initiating source. Reactions were also performed at temperatures over 100 °C in which the thermal initiation of styrene was used as an initiating source. In all cases, the polymerizations proceeded in a living manner, yielding polymers that showed an incremental increase in molecular weight with time and had narrow molecular weight distributions. Plots of number‐ average molecular weight versus conversion were linear, indicating a controlled polymerization. The resulting latices were colloidally stable and gave particle size distributions with a typical average particle diameter in the 150 nm range.